309LT1 FLUX CORED ARC WELDING WIRE for STAINLESS STEEL
Quantity: 10
- Beautiful Beads
- Join Mild Steel & Stainless Steel
- For AISI 304, 309 & 309L
Classification
AWS A 5.22 : E309LT1-1/4
Applications
Welding stainless steel to carbon steel or low alloy steel
YAWATA 309LT1 is a flux cored arc welding wire to be used with CO2 or AR+20% CO2 shield gas for joining stainless steel to carbon steel or low alloy steel. It provides excellent weldability, corrosion resistant and crack resistance due to proper ferrite contents in the deposited metal. Good slag removal, stable arc and easy to control. Weld metal has 23.5% Cr and 13% Ni.
EXTREMELY HIGH CRACK RESISTANCE
TYPICAL CHEMICAL COMPOSITION OF DEPOSITED METAL (%) | |||||||
SHIELD GAS | C | Si | Mn | P | S | Cr | Ni |
CO2 | 0.032 | 0.48 | 1.25 | 0.024 | 0.002 | 23.10 | 12.48 |
TYPICAL MECHANICAL PROPERTIES OF DEPOSITED METAL | ||
SHIELD GAS | TENSILE STRENGTH N/mm² (kgf/mm²) | ELONGATION % |
CO2 | 520 (56.8) | 37 |
SIZES & RECOMMENDED CURRENT RANGE (AC OR DC +) | |||||
DIAMETER (mm) | 1.2 | 1.6 | |||
WELDING POSITION | AMP | VOLT | AMP | VOLT | |
F, H-Fill | 100~300 | 20~36 | 200~360 | 26~40 | |
V-OH | 100~200 | 24~36 | - | - |
Inquiry - 309LT1 FLUX CORED ARC WELDING WIRE for STAINLESS STEEL