316LT1 Flux Core Wire for Stainless Steel
Quantity: 10
FOR 18%CR-12%NI-2%MO STAINLESS STEEL
- FOR AISI 316, 316L & 318
- BEAUTIFUL BEADS
- STABBLE ARC FORCE
- AWS A 5.22 : E316LT1-1/4
Welding 18%Cr-12%Ni-2%Mo stainless steel
YAWATA 316LT1 is a flux cored arc welding wire to be used with CO2 or AR+20% CO2 shield gas for welding critical chemical vessels and AISI 316L stainless steel. Weld metal is 18.5%Cr-12.5%Ni-2.5%Mo which provides excellent corrosion resistance.
HIGH CORROSION RESISTANCE
TYPICAL CHEMICAL COMPOSITION OF DEPOSITED METAL (%) | ||||||||
Shield Gas | C | Si | Mn | P | S | Cr | Ni | Mo |
CO2 | 0.037 | 0.44 | 1.16 | 0.030 | 0.005 | 18.17 | 12.48 | 2.35 |
TYPICAL MECHANICAL PROPERTIES OF DEPOSITED METAL | ||
Shield Gas | TENSILE STRENGTH N/mm² (kgf/mm²) | ELONGATION % |
CO2 | 520 (53) | 42 |
SIZES & RECOMMENDED CURRENT RANGE (DC ±) | ||||
DIAMETER (mm) | 1.2 | 1.6 | ||
WELDING POSITION | Amp | Volt | Amp | Volt |
F, H-fil | 100-300 | 20-36 | 200-360 | 26-40 |
V, OH | 100-200 | 24-36 | - | - |